Many bridges, buildings and road networks have not been treated with The CCI 4206 can be mixed at 1-2% with concrete to provide excellent corrosion inhibitory effect. The presence of the CCI 4206 molecules within the concrete make it highly corrosion inhibiting reducing the oxidation rate by 80-90% and hence increasing the life of the building from 5 – 10 times.The crack propagation in concrete is drastically reduced. The effect of corrosion inhibition is highly beneficial in coastal areas, rainy places where buildings remain damp all the time as well as in places having high humidity or having high salt content in soil and sand.
Figure 1 shows the metal weight loss or corrosion loss of steel rebar in salt water during an immersion test in salt water
Figure 2 shows the corrosion rate of steel rebar in salt water.
The rate of rebar corrosion on submerged structures in water or sea water drastically increases due to continuous exposure to dampness and wet concrete around the rebar. The CCI 4206 can be mixed at 1-2% with concrete to provide excellent corrosion inhibitory effect. The presence of the CCI 4206 molecules within the concrete make it highly corrosion inhibiting reducing the oxidation rate by 80-90% and hence increasing the life of the building from 5 - 10 times. The crack propagation in concrete is drastically reduced.
The dosage recommended is 20 kg per m3 of the admixture for normal environments and 40 kg/m3 for aggressive saline environments. The addition of the CCI 4206 does not have any detrimental effect on the setting time or compressive strength of the cement.
Concrete Corrosion Inhibitors for submerged structures, tunnels, infrastructure in wet environments, snow capped areas, saline exposure etc.
Concrete Corrosion Inhibiting Powder for Admixtures for Bridges, Flyovers, Roads and Buildings
Concrete Corrosion Inhibitors based upon food approved additives for addition in water tanks, concrete pipelines etc.
Concrete Corrosion Inhibiting Liquid for in-service infrastructure corrosion protection to reduce corrosion rate, spalling etc.